Injectable chemical anchor is a fast curing,multi-purpose,two components modified epoxy resin anchor system for threaded bars and reinforcing bars in both cracked and uncracked concrete.
| Ambient Temperature °C | Operable Time(min) | Curing Time(h) |
| -5 | 60 min | 72 h |
| 0 | 45 min | 48 h |
| 10 | 30 min | 24 h |
| 20 | 15 min | 12 h |
| ≥30 | 20 min | 6 h |
Injectable chemical anchor Performance Parameters
| Appearance A Part (Epoxy) | White paste |
| Appearance B Part (Hardener) | Red or black paste |
| Viscosity of mixture | 18-22 pa·s |
| Density after curing | 1.5±0.1 g/cm³ |
| Mixture ratio (weight ratio) | 3:1 |
Injectable chemical anchor Performance Indexes
| Colloidal Performance | Tensile strength (ASTMD638) | ≥55Mpa |
| Tensile modulus (ASTMD638) | ≥3500Mpa | |
| Elongation at break (ASTMD638) | ≥1.7% | |
| Flexural strength (ASTMD790) | ≥70Mpa | |
| Compressive strength (ASTMD695) | ≥82Mpa | |
| Thixotropy index | ≥4.0 | |
| Sagging mobility (25°C) | ≤2.0mm | |
| Distortion temperature | ≥65°C | |
| Adhesion Performance | Steel-steel tensile anti-shear strength | ≥16Mpa |
| Under the constraint drawing condition,ribbed steel bars and C30,Φ25,L=150mm tensile strength | ≥11Mpa | |
| Boding strength withc oncrete C60,Φ25,L=125mm | ≥17Mpa | |
| Steel-steel T impact stripping length | ≤25mm | |
| Non-volatile matter content (solid content) | ≥99% | |
| Long-term Performance | Wet and heat ageing | Compared with the short-term results at room temperature,the decrease rate of shears trength:≤12% |
| Heat aging resistance | Compared with the short-term results at same temperature 10 min,the decrease rateof shears trength:≤5% | |
| Freezing and thawing | Compared with room temperature,short-term results,the shear strength decrease rate is not greater than5% | |
| Fatigue stress | After 2×10^6 times continuous sine wave fatigue loads,specimen does not destroy | |
| Resistance to corrosion medium | Resistance to stress | Steel-steel tensile shear specimensdoes not destroy,and creep deformation value is less than 0.4mm |
| Alkaline medium | Compared with the control group,the strength does not decrease,and a sthe concrete damage,and shall not have cracks or come unglued | |
| Acid medium | Concrete damage,andshall not have cracks or degumming | |
●Modified epoxy resin,no styrene
●High strength & modulus,good toughness
●Aging resistance & thermal resistance
●Moisture tolerant,stable in a humid environment
●Acid & alkali resistance
●Seismic resistance,no expansion forces
●Excellent thixotropy,suitable for side and top anchoring
●Binocular straight mixed package,with special electric caulking gun and static mixer
●Planting steel bars and bolts in concrete structure
●Curtainwall & stone dry hanging brackets'reinforcement
●Building structure reinforcement & framework anchoring
●Various equipments'basic fixation
●Steel structures and concrete structures anchoring connection
●Reinforcement for highway,bridges,water conservancy projects rebuilding
●Reinforcement for advertisement boards,the noise barriers & barricades
●When stored correctly,the shelf life will be a tleast 12 months from the date of manufacture.Cartridges should be stored in their original packaging,the correct way up,in cool conditions (+50°Fto+77°F) and out of direct runlight.
Injectable chemical anchor is a fast curing,multi-purpose,two components modified epoxy resin anchor system for threaded bars and reinforcing bars in both cracked and uncracked concrete.
| Ambient Temperature °C | Operable Time(min) | Curing Time(h) |
| -5 | 60 min | 72 h |
| 0 | 45 min | 48 h |
| 10 | 30 min | 24 h |
| 20 | 15 min | 12 h |
| ≥30 | 20 min | 6 h |
Injectable chemical anchor Performance Parameters
| Appearance A Part (Epoxy) | White paste |
| Appearance B Part (Hardener) | Red or black paste |
| Viscosity of mixture | 18-22 pa·s |
| Density after curing | 1.5±0.1 g/cm³ |
| Mixture ratio (weight ratio) | 3:1 |
Injectable chemical anchor Performance Indexes
| Colloidal Performance | Tensile strength (ASTMD638) | ≥55Mpa |
| Tensile modulus (ASTMD638) | ≥3500Mpa | |
| Elongation at break (ASTMD638) | ≥1.7% | |
| Flexural strength (ASTMD790) | ≥70Mpa | |
| Compressive strength (ASTMD695) | ≥82Mpa | |
| Thixotropy index | ≥4.0 | |
| Sagging mobility (25°C) | ≤2.0mm | |
| Distortion temperature | ≥65°C | |
| Adhesion Performance | Steel-steel tensile anti-shear strength | ≥16Mpa |
| Under the constraint drawing condition,ribbed steel bars and C30,Φ25,L=150mm tensile strength | ≥11Mpa | |
| Boding strength withc oncrete C60,Φ25,L=125mm | ≥17Mpa | |
| Steel-steel T impact stripping length | ≤25mm | |
| Non-volatile matter content (solid content) | ≥99% | |
| Long-term Performance | Wet and heat ageing | Compared with the short-term results at room temperature,the decrease rate of shears trength:≤12% |
| Heat aging resistance | Compared with the short-term results at same temperature 10 min,the decrease rateof shears trength:≤5% | |
| Freezing and thawing | Compared with room temperature,short-term results,the shear strength decrease rate is not greater than5% | |
| Fatigue stress | After 2×10^6 times continuous sine wave fatigue loads,specimen does not destroy | |
| Resistance to corrosion medium | Resistance to stress | Steel-steel tensile shear specimensdoes not destroy,and creep deformation value is less than 0.4mm |
| Alkaline medium | Compared with the control group,the strength does not decrease,and a sthe concrete damage,and shall not have cracks or come unglued | |
| Acid medium | Concrete damage,andshall not have cracks or degumming | |
●Modified epoxy resin,no styrene
●High strength & modulus,good toughness
●Aging resistance & thermal resistance
●Moisture tolerant,stable in a humid environment
●Acid & alkali resistance
●Seismic resistance,no expansion forces
●Excellent thixotropy,suitable for side and top anchoring
●Binocular straight mixed package,with special electric caulking gun and static mixer
●Planting steel bars and bolts in concrete structure
●Curtainwall & stone dry hanging brackets'reinforcement
●Building structure reinforcement & framework anchoring
●Various equipments'basic fixation
●Steel structures and concrete structures anchoring connection
●Reinforcement for highway,bridges,water conservancy projects rebuilding
●Reinforcement for advertisement boards,the noise barriers & barricades
●When stored correctly,the shelf life will be a tleast 12 months from the date of manufacture.Cartridges should be stored in their original packaging,the correct way up,in cool conditions (+50°Fto+77°F) and out of direct runlight.