Self Leveling polyurethane sealant is one component sealant with low modulus and excellent elasticity. Self Leveling polyurethane sealant is especially suitable for sealing joints for the multi-porous materials.
| Model | TP630 | ||
| Class | 25LM self-leveling | ||
| Colors | Concrete Grey,White | ||
| Density | 1.3~1.4KG/L | ||
| Tack free time | 45-120 min,depending on weather | ||
| Curing time | ≥2mm/24h | ||
| Hardness Shore A | around 25 | ||
| Modulus(100% Elongation) | 23℃ | ≤0.4Mpa | |
| -20℃ | ≤0.6Mpa | ||
| Leveling property | Smooth and leveling | ||
| Extrudability (ml/min) | ≥80 | ||
| Elastic Recovery | ≥70% | ||
| Elongation at break | >600% | ||
| Service Temperature | -40-90℃(minimum 50℃ in hot water) | ||
Tensile Properties at maintained extension | No breaking | ||
Tensilepro perties at maintained extension (afterwaterimmersion) | No breaking | ||
| Tensile properties(cold extension-hot compression) | No breaking | ||
| Loss ofmass%(≤) | 8 | ||
| Application Temperature | 5°C-35°C | ||
| Service Temperature | -40°C+90°C(minimum 50°C in hot water) | ||
●Excellent adhesion with former cleaned PU sealant.
●One Component,ready-to-use.
●Good adhesion with concrete materials.
●Fast cure.
●Good weathering resistance and high durability.
●No pollution.
●Can be painted.
●Sealing joints in the concrete roads and bridges.
●General sealing for construction joints.
●Sealing joints in the airport runway.
●Repairing and sealing the crack of buildings.
●Keep contents of out of reach of children.In case of contact with eyes,please rinse eyes with plently of water and seek medical advice as soon as possible.
●9 months stored at dry below 25℃ unopened in original containers.
Self Leveling polyurethane sealant is one component sealant with low modulus and excellent elasticity. Self Leveling polyurethane sealant is especially suitable for sealing joints for the multi-porous materials.
| Model | TP630 | ||
| Class | 25LM self-leveling | ||
| Colors | Concrete Grey,White | ||
| Density | 1.3~1.4KG/L | ||
| Tack free time | 45-120 min,depending on weather | ||
| Curing time | ≥2mm/24h | ||
| Hardness Shore A | around 25 | ||
| Modulus(100% Elongation) | 23℃ | ≤0.4Mpa | |
| -20℃ | ≤0.6Mpa | ||
| Leveling property | Smooth and leveling | ||
| Extrudability (ml/min) | ≥80 | ||
| Elastic Recovery | ≥70% | ||
| Elongation at break | >600% | ||
| Service Temperature | -40-90℃(minimum 50℃ in hot water) | ||
Tensile Properties at maintained extension | No breaking | ||
Tensilepro perties at maintained extension (afterwaterimmersion) | No breaking | ||
| Tensile properties(cold extension-hot compression) | No breaking | ||
| Loss ofmass%(≤) | 8 | ||
| Application Temperature | 5°C-35°C | ||
| Service Temperature | -40°C+90°C(minimum 50°C in hot water) | ||
●Excellent adhesion with former cleaned PU sealant.
●One Component,ready-to-use.
●Good adhesion with concrete materials.
●Fast cure.
●Good weathering resistance and high durability.
●No pollution.
●Can be painted.
●Sealing joints in the concrete roads and bridges.
●General sealing for construction joints.
●Sealing joints in the airport runway.
●Repairing and sealing the crack of buildings.
●Keep contents of out of reach of children.In case of contact with eyes,please rinse eyes with plently of water and seek medical advice as soon as possible.
●9 months stored at dry below 25℃ unopened in original containers.