Road Bridge And Airport Runway polyurethane sealant is one component salant with low modulus and excellent elasticity.It is especially suitable for sealing joints for the multi-porous materials.
| Model | TP620 | ||
| Class | 25LM non-flowing | ||
| Colors | Concrete Grey,White | ||
| Density | 1.3~1.4KG/L | ||
| Tack free time | 45-120 min,depending on weather | ||
| Curing time | ≥2mm/24h | ||
| Hardness Shore A | around 25 | ||
| Modulus(100% Elongation) | 23℃ | ≤0.4Mpa | |
| -20℃ | ≤0.6Mpa | ||
| Leveling property | ≥70% | ||
| Slump/mm | Vertical | ≤3 | |
| HorizontalHorizontalorizontalorizontal | Nodeformation | ||
| Extrudability (ml/min) | ≥80 | ||
| Elastic Recovery | ≥70% | ||
| Elongation at break | >600% | ||
| Service Temperature | -40-90℃(minimum 50℃ in hot water) | ||
Tensile Properties at maintained extension | No breaking | ||
Tensilepro perties at maintained extension (afterwaterimmersion) | No breaking | ||
| Tensile properties(cold extension-hot compression) | No breaking | ||
| Loss ofmass%(≤) | 8 | ||
| Application Temperature | 5°C-35°C | ||
| Service Temperature | -40°C+90°C(minimum 50°C in hot water) | ||
●Excellent adhesion with former cleaned PU sealant.
●One Component,ready to use.
●Good adhesion with concrete materials.
●Fastcure.
●Good weathering resistance and high durability.
●No pollution
●Can be painted
●Sealing joints in the concrete roads and bridges.
●General sealing for construction joints.
●Sealing joints in the airport runway.
●Repairing and sealing the crack of buildings.
●Keep contents of out of reach of children.In case of contact with eyes,please rinse eyes with plently of water and seek medical advice as soon as possible.
●9 months stored at dry below 25℃ unopened in original containers.
Road Bridge And Airport Runway polyurethane sealant is one component salant with low modulus and excellent elasticity.It is especially suitable for sealing joints for the multi-porous materials.
| Model | TP620 | ||
| Class | 25LM non-flowing | ||
| Colors | Concrete Grey,White | ||
| Density | 1.3~1.4KG/L | ||
| Tack free time | 45-120 min,depending on weather | ||
| Curing time | ≥2mm/24h | ||
| Hardness Shore A | around 25 | ||
| Modulus(100% Elongation) | 23℃ | ≤0.4Mpa | |
| -20℃ | ≤0.6Mpa | ||
| Leveling property | ≥70% | ||
| Slump/mm | Vertical | ≤3 | |
| HorizontalHorizontalorizontalorizontal | Nodeformation | ||
| Extrudability (ml/min) | ≥80 | ||
| Elastic Recovery | ≥70% | ||
| Elongation at break | >600% | ||
| Service Temperature | -40-90℃(minimum 50℃ in hot water) | ||
Tensile Properties at maintained extension | No breaking | ||
Tensilepro perties at maintained extension (afterwaterimmersion) | No breaking | ||
| Tensile properties(cold extension-hot compression) | No breaking | ||
| Loss ofmass%(≤) | 8 | ||
| Application Temperature | 5°C-35°C | ||
| Service Temperature | -40°C+90°C(minimum 50°C in hot water) | ||
●Excellent adhesion with former cleaned PU sealant.
●One Component,ready to use.
●Good adhesion with concrete materials.
●Fastcure.
●Good weathering resistance and high durability.
●No pollution
●Can be painted
●Sealing joints in the concrete roads and bridges.
●General sealing for construction joints.
●Sealing joints in the airport runway.
●Repairing and sealing the crack of buildings.
●Keep contents of out of reach of children.In case of contact with eyes,please rinse eyes with plently of water and seek medical advice as soon as possible.
●9 months stored at dry below 25℃ unopened in original containers.