TP640-220/400
TENGYU
310ml 600ml
White,Black,Grey etc.
| Quantity: | |
|---|---|
Model | TP-220 | TP-400 | |
Solid Content ≥85% | 99.2 | 99.8 | |
Density (g/cm3) | 1.33 | 1.4 | |
Sagging（mm）≦2 | 0 | ||
Tack free time(h) ≤24 | 4.4 | 2.5 | |
7d Tensile Adhesive Strength (MPa) ≧0.4 | 1 | 0.8 | |
Low temperature flexiblility | No Cracking | ||
Tensile Strength (MPa) ≧0.5 | 3.98 | 2.8 | |
Elongation at break ≧400% | 621 | 807 | |
Volume expansion ratio | 326% | 422% | |
Long-term soaking volume expansion ratio retention ) ≧90% | 99 | 101 | |
Water pressure resistance (no water seepage) | No water | No water | |
Thickness after full dry(mm) ≧2 | 2.52 | 3.2 | |
Harmful material limit | VOC g/L | 16 | |
The free toluene diisocyanate (TDI) g/kg | 0 | ||
Good water-stopping effect: it has the elastic sealing water of rubber and the double sealing water stopping mechanism of its own volume expansion and water stop after water,and can resist water pressure of 2.5MPa.
Good expansion: high expansion rate,reaching more than 220% or 400%.
Convenient construction: single component,glue,standard caulking gun can be used.
Construction tight&close: firmly attached to the concrete surface regardless of whether the base surface is wet, smooth or rough.
Safe & non toxic: it is an environmentally friendly product in contact with drinking water.
Cost effective: The performance is better than the traditional construction joint waterproof material,such as steel edge rubber water-stop glue or tape,the price is reasonable.
Railway tunnels,road tunnels,urban subways,underground structures of buildings,sewage treatment tanks,etc.
The construction joints of various underground structures are waterproof.
The underground structure is watered after the pouring.
All kinds of pre-buried pipelines,through-wall steel bars,H-beams,pile caps and other waterproof.
Various types of construction joints or structural cracks are leaked.
Keep contents out of reach of children.
12 months stored at dry below25°C unopened in original containers.
Model | TP-220 | TP-400 | |
Solid Content ≥85% | 99.2 | 99.8 | |
Density (g/cm3) | 1.33 | 1.4 | |
Sagging（mm）≦2 | 0 | ||
Tack free time(h) ≤24 | 4.4 | 2.5 | |
7d Tensile Adhesive Strength (MPa) ≧0.4 | 1 | 0.8 | |
Low temperature flexiblility | No Cracking | ||
Tensile Strength (MPa) ≧0.5 | 3.98 | 2.8 | |
Elongation at break ≧400% | 621 | 807 | |
Volume expansion ratio | 326% | 422% | |
Long-term soaking volume expansion ratio retention ) ≧90% | 99 | 101 | |
Water pressure resistance (no water seepage) | No water | No water | |
Thickness after full dry(mm) ≧2 | 2.52 | 3.2 | |
Harmful material limit | VOC g/L | 16 | |
The free toluene diisocyanate (TDI) g/kg | 0 | ||
Good water-stopping effect: it has the elastic sealing water of rubber and the double sealing water stopping mechanism of its own volume expansion and water stop after water,and can resist water pressure of 2.5MPa.
Good expansion: high expansion rate,reaching more than 220% or 400%.
Convenient construction: single component,glue,standard caulking gun can be used.
Construction tight&close: firmly attached to the concrete surface regardless of whether the base surface is wet, smooth or rough.
Safe & non toxic: it is an environmentally friendly product in contact with drinking water.
Cost effective: The performance is better than the traditional construction joint waterproof material,such as steel edge rubber water-stop glue or tape,the price is reasonable.
Railway tunnels,road tunnels,urban subways,underground structures of buildings,sewage treatment tanks,etc.
The construction joints of various underground structures are waterproof.
The underground structure is watered after the pouring.
All kinds of pre-buried pipelines,through-wall steel bars,H-beams,pile caps and other waterproof.
Various types of construction joints or structural cracks are leaked.
Keep contents out of reach of children.
12 months stored at dry below25°C unopened in original containers.